U.S Specifications – Foamed Concrete Specialists - Propump Engineering Ltd

U.S Specifications

Neat Cement

Mix0;1;0.6
Wet Density Kg/m³19
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³270
Cement % Cube5
Water Kg/m³155
Water % Cube10
Foam litres 50grms/l1375
Foam % Cube85
Chemical litres @2.5%0.1.71
Strength N/mm2 @ 28 Days72.5
Thermal Insulation W/m.K0.08
Shrinkage %0.38
E modulas @ 90 days Mpa300
Mix0;1;0.6
Wet Density Kg/m³25
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³380
Cement % Cube7
Water Kg/m³220
Water % Cube14
Foam litres 50grms/l1280
Foam % Cube79
Chemical litres @2.5%1.61
Strength N/mm2 @ 28 Days145
Thermal Insulation W/m.K0.09
Shrinkage %0.30
E modulas @ 90 days Mpa600
Mix0;1;0.6
Wet Density Kg/m³31
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³490
Cement % Cube9
Water Kg/m³280
Water % Cube14
Foam litres 50grms/l1185
Foam % Cube73
Chemical litres @2.5%1.48
Strength N/mm2 @ 28 Days290
Thermal Insulation W/m.K0.10
Shrinkage %0.27
E modulas @ 90 days Mpa1000
Mix0;1;0.6
Wet Density Kg/m³37.5
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³600
Cement % Cube11
Water Kg/m³340
Water % Cube21
Foam litres 50grms/l1090
Foam % Cube68
Chemical litres @2.5%1.35
Strength N/mm2 @ 28 Days435
Thermal Insulation W/m.K0.11
Shrinkage %0.22
E modulas @ 90 days Mpa1600
Mix0;1;0.6
Wet Density Kg/m³44
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³710
Cement % Cube13
Water Kg/m³405
Water % Cube25
Foam litres 50grms/l995
Foam % Cube62
Chemical litres @2.5%1.24
Strength N/mm2 @ 28 Days580
Thermal Insulation W/m.K0.13
Shrinkage %0.21
E modulas @ 90 days Mpa2400
Mix0;1;0.6
Wet Density Kg/m³50
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³810
Cement % Cube15
Water Kg/m³470
Water % Cube29
Foam litres 50grms/l900
Foam % Cube56
Chemical litres @2.5%1.13
Strength N/mm2 @ 28 Days725
Thermal Insulation W/m.K0.15
Shrinkage %0.20
E modulas @ 90 days Mpa3300

1:1 Sand / Cement mix

Mix1;1;0.6
Wet Density Kg/m³37.5
Sand 2mm max Kg/m³365
Sand % Cube8
Cement 52.5N Kg/m³365
Cement % Cube7
Water Kg/m³210
Water % Cube13
Foam litres 50grms/l1160
Foam % Cube72
Chemical litres @2.5%1.45
Strength N/mm2 @ 28 Days246.5
Thermal Insulation W/m.K0.11
Shrinkage %0.22
E modulas @ 90 days Mpa1300
Mix1;1;0.6
Wet Density Kg/m³44
Sand 2mm max Kg/m³430
Sand % Cube10
Cement 52.5N Kg/m³430
Cement % Cube8
Water Kg/m³245
Water % Cube15
Foam litres 50grms/l1080
Foam % Cube67
Chemical litres @2.5%1.35
Strength N/mm2 @ 28 Days362.5
Thermal Insulation W/m.K0.13
Shrinkage %0.21
E modulas @ 90 days Mpa1800
Mix1;1;0.6
Wet Density Kg/m³50
Sand 2mm max Kg/m³500
Sand % Cube12
Cement 52.5N Kg/m³500
Cement % Cube9
Water Kg/m³285
Water % Cube17
Foam litres 50grms/l995
Foam % Cube62
Chemical litres @2.5%1.24
Strength N/mm2 @ 28 Days464
Thermal Insulation W/m.K0.15
Shrinkage %0.20
E modulas @ 90 days Mpa2500
Mix1;1;0.6
Wet Density Kg/m³56
Sand 2mm max Kg/m³565
Sand % Cube13
Cement 52.5N Kg/m³565
Cement % Cube10
Water Kg/m³325
Water % Cube20
Foam litres 50grms/l910
Foam % Cube57
Chemical litres @2.5%1.13
Strength N/mm2 @ 28 Days609
Thermal Insulation W/m.K0.17
Shrinkage %0.19
E modulas @ 90 days Mpa3500
Mix1;1;0.6
Wet Density Kg/m³62
Sand 2mm max Kg/m³630
Sand % Cube14
Cement 52.5N Kg/m³630
Cement % Cube12
Water Kg/m³360
Water % Cube22
Foam litres 50grms/l830
Foam % Cube52
Chemical litres @2.5%1.03
Strength N/mm2 @ 28 Days797.5
Thermal Insulation W/m.K0.20
Shrinkage %0.18
E modulas @ 90 days Mpa4500

2:1 Sand / Cement mix

Mix1;1;0.6
Wet Density Kg/m³44
Sand 2mm max Kg/m³620
Sand % Cube14
Cement 52.5N Kg/m³310
Cement % Cube6
Water Kg/m³175
Water % Cube11
Foam litres 50grms/l1115
Foam % Cube69
Chemical litres @2.5%1.39
Strength N/mm2 @ 28 Days217.5
Thermal Insulation W/m.K0.13
Shrinkage %0.21
E modulas @ 90 days Mpa1700
Mix2;1;0.6
Wet Density Kg/m³50
Sand 2mm max Kg/m³720
Sand % Cube16
Cement 52.5N Kg/m³360
Cement % Cube7
Water Kg/m³205
Water % Cube13
Foam litres 50grms/l1040
Foam % Cube64
Chemical litres @2.5%1.29
Strength N/mm2 @ 28 Days319
Thermal Insulation W/m.K0.15
Shrinkage %0.20
E modulas @ 90 days Mpa2300
Mix2;1;0.6
Wet Density Kg/m³56
Sand 2mm max Kg/m³810
Sand % Cube18
Cement 52.5N Kg/m³405
Cement % Cube8
Water Kg/m³230
Water % Cube14
Foam litres 50grms/l960
Foam % Cube60
Chemical litres @2.5%1.21
Strength N/mm2 @ 28 Days435
Thermal Insulation W/m.K0.17
Shrinkage %0.19
E modulas @ 90 days Mpa2900
Mix2;1;0.6
Wet Density Kg/m³62
Sand 2mm max Kg/m³910
Sand % Cube20
Cement 52.5N Kg/m³455
Cement % Cube9
Water Kg/m³260
Water % Cube16
Foam litres 50grms/l885
Foam % Cube55
Chemical litres @2.5%1.10
Strength N/mm2 @ 28 Days580
Thermal Insulation W/m.K0.20
Shrinkage %0.18
E modulas @ 90 days Mpa3800
Mix2;1;0.6
Wet Density Kg/m³68
Sand 2mm max Kg/m³1000
Sand % Cube22
Cement 52.5N Kg/m³500
Cement % Cube10
Water Kg/m³290
Water % Cube18
Foam litres 50grms/l805
Foam % Cube50
Chemical litres @2.5%1.0
Strength N/mm2 @ 28 Days696
Thermal Insulation W/m.K0.23
Shrinkage %0.15
E modulas @ 90 days Mpa4800
Mix2;1;0.6
Wet Density Kg/m³75
Sand 2mm max Kg/m³1100
Sand % Cube24
Cement 52.5N Kg/m³550
Cement % Cube11
Water Kg/m³315
Water % Cube20
Foam litres 50grms/l730
Foam % Cube45
Chemical litres @2.5%0.92
Strength N/mm2 @ 28 Days870
Thermal Insulation W/m.K0.27
Shrinkage %0.11
E modulas @ 90 days Mpa6000
Mix2;1;0.6
Wet Density Kg/m³81
Sand 2mm max Kg/m³1190
Sand % Cube27
Cement 52.5N Kg/m³595
Cement % Cube11
Water Kg/m³345
Water % Cube21
Foam litres 50grms/l655
Foam % Cube41
Chemical litres @2.5%0.8
Strength N/mm2 @ 28 Days1044
Thermal Insulation W/m.K0.35
Shrinkage %0.10
E modulas @ 90 days Mpa7500
Mix2;1;0.6
Wet Density Kg/m³87
Sand 2mm max Kg/m³1290
Sand % Cube29
Cement 52.5N Kg/m³645
Cement % Cube12
Water Kg/m³370
Water % Cube23
Foam litres 50grms/l580
Foam % Cube36
Chemical litres @2.5%0.72
Strength N/mm2 @ 28 Days1232.5
Thermal Insulation W/m.K0.47
Shrinkage %0.09
E modulas @ 90 days Mpa9000
Mix2;1;0.6
Wet Density Kg/m³94
Sand 2mm max Kg/m³1390
Sand % Cube31
Cement 52.5N Kg/m³695
Cement % Cube13
Water Kg/m³400
Water % Cube25
Foam litres 50grms/l500
Foam % Cube31
Chemical litres @2.5%0.61
Strength N/mm2 @ 28 Days1450
Thermal Insulation W/m.K0.55
Shrinkage %1.08
E modulas @ 90 days Mpa10500

3:1 Sand / Cement mix

Mix3;1;0.6
Wet Density Kg/m³68
Sand 2mm max Kg/m³1180
Sand % Cube26
Cement 52.5N Kg/m³395
Cement % Cube8
Water Kg/m³225
Water % Cube14
Foam litres 50grms/l840
Foam % Cube52
Chemical litres @2.5%1.05
Strength N/mm2 @ 28 Days435
Thermal Insulation W/m.K0.23
Shrinkage %0.15
E modulas @ 90 days Mpa4200
Mix3;1;0.6
Wet Density Kg/m³75
Sand 2mm max Kg/m³1290
Sand % Cube29
Cement 52.5N Kg/m³430
Cement % Cube8
Water Kg/m³250
Water % Cube15
Foam litres 50grms/l765
Foam % Cube48
Chemical litres @2.5%0.96
Strength N/mm2 @ 28 Days580
Thermal Insulation W/m.K0.27
Shrinkage %0.11
E modulas @ 90 days Mpa5200
Mix3;1;0.6
Wet Density Kg/m³81
Sand 2mm max Kg/m³1400
Sand % Cube31
Cement 52.5N Kg/m³465
Cement % Cube9
Water Kg/m³270
Water % Cube17
Foam litres 50grms/l695
Foam % Cube43
Chemical litres @2.5%0.87
Strength N/mm2 @ 28 Days725
Thermal Insulation W/m.K0.35
Shrinkage %0.10
E modulas @ 90 days Mpa6500
Mix3;1;0.6
Wet Density Kg/m³87
Sand 2mm max Kg/m³1515
Sand % Cube34
Cement 52.5N Kg/m³505
Cement % Cube10
Water Kg/m³290
Water % Cube18
Foam litres 50grms/l620
Foam % Cube38
Chemical litres @2.5%0.77
Strength N/mm2 @ 28 Days942.5
Thermal Insulation W/m.K0.47
Shrinkage %0.09
E modulas @ 90 days Mpa7800
Mix3;1;0.6
Wet Density Kg/m³94
Sand 2mm max Kg/m³1630
Sand % Cube37
Cement 52.5N Kg/m³540
Cement % Cube10
Water Kg/m³310
Water % Cube19
Foam litres 50grms/l546
Foam % Cube34
Chemical litres @2.5%0.67
Strength N/mm2 @ 28 Days1160
Thermal Insulation W/m.K0.55
Shrinkage %0.08
E modulas @ 90 days Mpa9400
Mix3;1;0.6
Wet Density Kg/m³100
Sand 2mm max Kg/m³1730
Sand % Cube39
Cement 52.5N Kg/m³575
Cement % Cube11
Water Kg/m³330
Water % Cube21
Foam litres 50grms/l471
Foam % Cube29
Chemical litres @2.5%0.58
Strength N/mm2 @ 28 Days1377.5
Thermal Insulation W/m.K0.65
Shrinkage %0.07
E modulas @ 90 days Mpa11300
Mix3;1;0.6
Wet Density Kg/m³106
Sand 2mm max Kg/m³1850
Sand % Cube42
Cement 52.5N Kg/m³615
Cement % Cube11
Water Kg/m³355
Water % Cube22
Foam litres 50grms/l400
Foam % Cube25
Chemical litres @2.5%0.50
Strength N/mm2 @ 28 Days1740
Thermal Insulation W/m.K0.75
Shrinkage %0.05
E modulas @ 90 days Mpa13500
Mix3;1;0.6
Wet Density Kg/m³112
Sand 2mm max Kg/m³1970
Sand % Cube44
Cement 52.5N Kg/m³615
Cement % Cube131
Water Kg/m³380
Water % Cube23
Foam litres 50grms/l325
Foam % Cube20
Chemical litres @2.5%0.40
Strength N/mm2 @ 28 Days2030
Thermal Insulation W/m.K0.85
Shrinkage %0.04
E modulas @ 90 days Mpa16000

More information

Propump Consultancy Services

Propump Engineering foamed concrete specialists site visits and consultancy services
Propump Engineering foamed concrete specialists site visits and consultancy services

Propump news & articles

Foam concrete inline production system enable the most accurate and efficient method of manufacturing foam concretes on-site
Foam concrete inline production system enable the most accurate and efficient method of manufacturing foam concretes on-site

Why choose foamed concrete?

Foamed Concrete Applications include filling of sink holes and other ground movement to support the underside of structures
Foamed concrete Applications including the use of fluid and free flowing material for the use in ground stabilisation and mass infill

Projects by Propump

Foamed concrete used for Crossrail tunnelling works, foamed concrete filling addits, tunnels and TBM machines
Foamed concrete used for Crossrail tunnelling works, foamed concrete filling addits, tunnels and TBM machines