European Specifications – Foamed Concrete Specialists - Propump Engineering Ltd

European Specifications

Neat Cement

Mix0;1;0.6
Wet Density Kg/m³300
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³160
Cement % Cube5
Water Kg/m³96
Water % Cube10
Foam litres 50grms/l852
Foam % Cube85
Chemical litres @2.5%1.06
Strength N/mm2 @ 28 Days0.5
Thermal Insulation W/m.K0.08
Shrinkage %0.38
E modulus @ 90 days Mpa300
Mix0;1;0.6
Wet Density Kg/m³400
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³225
Cement % Cube7
Water Kg/m³135
Water % Cube14
Foam litres 50grms/l794
Foam % Cube79
Chemical litres @2.5%1.0
Strength N/mm2 @ 28 Days1.0
Thermal Insulation W/m.K0.09
Shrinkage %0.30
E modulus @ 90 days Mpa600

Mix0;1;0.6
Wet Density Kg/m³500
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³290
Cement % Cube9
Water Kg/m³175
Water % Cube18
Foam litres 50grms/l734
Foam % Cube73
Chemical litres @2.5%0.92
Strength N/mm2 @ 28 Days2.0
Thermal Insulation W/m.K0.1
Shrinkage %0.27
E modulus @ 90 days Mpa1000
Mix0;1;0.6
Wet Density Kg/m³600
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³335
Cement % Cube11
Water Kg/m³210
Water % Cube21
Foam litres 50grms/l675
Foam % Cube68
Chemical litres @2.5%0.84
Strength N/mm2 @ 28 Days3.0
Thermal Insulation W/m.K0.11
Shrinkage %0.22
E modulus @ 90 days Mpa1600
Mix0;1;0.6
Wet Density Kg/m³700
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³420
Cement % Cube13
Water Kg/m³250
Water % Cube25
Foam litres 50grms/l616
Foam % Cube62
Chemical litres @2.5%0.77
Strength N/mm2 @ 28 Days4.0
Thermal Insulation W/m.K0.13
Shrinkage %0.21
E modulus @ 90 days Mpa2400
Mix0;1;0.6
Wet Density Kg/m³800
Sand 2mm max Kg/m³0
Sand % Cube0
Cement 52.5N Kg/m³482
Cement % Cube15
Water Kg/m³290
Water % Cube29
Foam litres 50grms/l557
Foam % Cube56
Chemical litres @2.5%0.70
Strength N/mm2 @ 28 Days5.0
Thermal Insulation W/m.K0.15
Shrinkage %0.20
E modulus @ 90 days Mpa3300

1:1 Sand / Cement mix

Mix1;1;0.6
Wet Density Kg/m³600
Sand 2mm max Kg/m³216
Sand % Cube8
Cement 52.5N Kg/m³216
Cement % Cube7
Water Kg/m³130
Water % Cube13
Foam litres 50grms/l719
Foam % Cube72
Chemical litres @2.5%0.90
Strength N/mm2 @ 28 Days1.0
Thermal Insulation W/m.K0.11
Shrinkage %0.22
E modulus @ 90 days Mpa1300
Mix1;1;0.6
Wet Density Kg/m³700
Sand 2mm max Kg/m³256
Sand % Cube10
Cement 52.5N Kg/m³256
Cement % Cube8
Water Kg/m³153
Water % Cube15
Foam litres 50grms/l668
Foam % Cube67
Chemical litres @2.5%0.84
Strength N/mm2 @ 28 Days1.5
Thermal Insulation W/m.K0.13
Shrinkage %0.21
E modulus @ 90 days Mpa1800
Mix1;1;0.6
Wet Density Kg/m³800
Sand 2mm max Kg/m³295
Sand % Cube12
Cement 52.5N Kg/m³295
Cement % Cube9
Water Kg/m³177
Water % Cube17
Foam litres 50grms/l617
Foam % Cube62
Chemical litres @2.5%0.77
Strength N/mm2 @ 28 Days2
Thermal Insulation W/m.K0.15
Shrinkage %0.20
E modulus @ 90 days Mpa2500
Mix1;1;0.6
Wet Density Kg/m³900
Sand 2mm max Kg/m³335
Sand % Cube13
Cement 52.5N Kg/m³335
Cement % Cube10
Water Kg/m³200
Water % Cube20
Foam litres 50grms/l565
Foam % Cube57
Chemical litres @2.5%0.70
Strength N/mm2 @ 28 Days3
Thermal Insulation W/m.K0.17
Shrinkage %0.19
E modulus @ 90 days Mpa3500
Mix1;1;0.6
Wet Density Kg/m³1000
Sand 2mm max Kg/m³375
Sand % Cube14
Cement 52.5N Kg/m³375
Cement % Cube12
Water Kg/m³224
Water % Cube22
Foam litres 50grms/l515
Foam % Cube52
Chemical litres @2.5%0.64
Strength N/mm2 @ 28 Days4
Thermal Insulation W/m.K0.2
Shrinkage %0.18
E modulus @ 90 days Mpa4500

2:1 Sand / Cement mix

Mix2;1;0.6
Wet Density Kg/m³700
Sand 2mm max Kg/m³370
Sand % Cube14
Cement 52.5N Kg/m³185
Cement % Cube6
Water Kg/m³110
Water % Cube11
Foam litres 50grms/l690
Foam % Cube69
Chemical litres @2.5%0.86
Strength N/mm2 @ 28 Days0.7
Thermal Insulation W/m.K0.13
Shrinkage %0.21
E modulus @ 90 days Mpa1700
Mix2;1;0.6
Wet Density Kg/m³800
Sand 2mm max Kg/m³426
Sand % Cube16
Cement 52.5N Kg/m³213
Cement % Cube7
Water Kg/m³127
Water % Cube13
Foam litres 50grms/l643
Foam % Cube64
Chemical litres @2.5%0.80
Strength N/mm2 @ 28 Days0.90
Thermal Insulation W/m.K0.15
Shrinkage %0.20
E modulus @ 90 days Mpa2300
Mix2;1;0.6
Wet Density Kg/m³900
Sand 2mm max Kg/m³482
Sand % Cube18
Cement 52.5N Kg/m³241
Cement % Cube8
Water Kg/m³144
Water % Cube14
Foam litres 50grms/l596
Foam % Cube60
Chemical litres @2.5%0.75
Strength N/mm2 @ 28 Days1.2
Thermal Insulation W/m.K0.17
Shrinkage %0.19
E modulus @ 90 days Mpa2900
Mix2;1;0.6
Wet Density Kg/m³1000
Sand 2mm max Kg/m³540
Sand % Cube20
Cement 52.5N Kg/m³270
Cement % Cube9
Water Kg/m³160
Water % Cube16
Foam litres 50grms/l548
Foam % Cube55
Chemical litres @2.5%0.68
Strength N/mm2 @ 28 Days1.6
Thermal Insulation W/m.K0.2
Shrinkage %0.18
E modulus @ 90 days Mpa3800
Mix2;1;0.6
Wet Density Kg/m³1100
Sand 2mm max Kg/m³596
Sand % Cube22
Cement 52.5N Kg/m³298
Cement % Cube10
Water Kg/m³180
Water % Cube18
Foam litres 50grms/l500
Foam % Cube50
Chemical litres @2.5%0.62
Strength N/mm2 @ 28 Days2.2
Thermal Insulation W/m.K0.23
Shrinkage %0.15
E modulus @ 90 days Mpa4800
Mix2;1;0.6
Wet Density Kg/m³1200
Sand 2mm max Kg/m³653
Sand % Cube24
Cement 52.5N Kg/m³326
Cement % Cube11
Water Kg/m³195
Water % Cube20
Foam litres 50grms/l453
Foam % Cube45
Chemical litres @2.5%0.57
Strength N/mm2 @ 28 Days3
Thermal Insulation W/m.K0.27
Shrinkage %0.11
E modulus @ 90 days Mpa6000
Mix2;1;0.6
Wet Density Kg/m³1300
Sand 2mm max Kg/m³709
Sand % Cube27
Cement 52.5N Kg/m³354
Cement % Cube11
Water Kg/m³213
Water % Cube21
Foam litres 50grms/l405
Foam % Cube41
Chemical litres @2.5%0.50
Strength N/mm2 @ 28 Days4
Thermal Insulation W/m.K0.35
Shrinkage %0.10
E modulus @ 90 days Mpa7500
Mix2;1;0.6
Wet Density Kg/m³1400
Sand 2mm max Kg/m³766
Sand % Cube29
Cement 52.5N Kg/m³383
Cement % Cube12
Water Kg/m³230
Water % Cube23
Foam litres 50grms/l358
Foam % Cube36
Chemical litres @2.5%0.45
Strength N/mm2 @ 28 Days5.4
Thermal Insulation W/m.K0.47
Shrinkage %0.09
E modulus @ 90 days Mpa9000
Mix2;1;0.6
Wet Density Kg/m³1500
Sand 2mm max Kg/m³824
Sand % Cube31
Cement 52.5N Kg/m³412
Cement % Cube13
Water Kg/m³247
Water % Cube25
Foam litres 50grms/l309
Foam % Cube31
Chemical litres @2.5%0.38
Strength N/mm2 @ 28 Days7.2
Thermal Insulation W/m.K0.55
Shrinkage %1.08
E modulus @ 90 days Mpa10500

3:1 Sand / Cement mix

Mix3;1;0.6
Wet Density Kg/m³1100
Sand 2mm max Kg/m³700
Sand % Cube26
Cement 52.5N Kg/m³235
Cement % Cube8
Water Kg/m³140
Water % Cube14
Foam litres 50grms/l520
Foam % Cube52
Chemical litres @2.5%0.65
Strength N/mm2 @ 28 Days2.2
Thermal Insulation W/m.K0.23
Shrinkage %0.15
E modulus @ 90 days Mpa4200
Mix3;1;0.6
Wet Density Kg/m³1200
Sand 2mm max Kg/m³766
Sand % Cube29
Cement 52.5N Kg/m³255
Cement % Cube8
Water Kg/m³153
Water % Cube15
Foam litres 50grms/l475
Foam % Cube48
Chemical litres @2.5%0.60
Strength N/mm2 @ 28 Days2.8
Thermal Insulation W/m.K0.27
Shrinkage %0.11
E modulus @ 90 days Mpa5200
Mix3;1;0.6
Wet Density Kg/m³1300
Sand 2mm max Kg/m³832
Sand % Cube31
Cement 52.5N Kg/m³277
Cement % Cube9
Water Kg/m³166
Water % Cube17
Foam litres 50grms/l430
Foam % Cube43
Chemical litres @2.5%0.54
Strength N/mm2 @ 28 Days3.6
Thermal Insulation W/m.K0.35
Shrinkage %0.10
E modulus @ 90 days Mpa6500
Mix3;1;0.6
Wet Density Kg/m³1400
Sand 2mm max Kg/m³900
Sand % Cube34
Cement 52.5N Kg/m³300
Cement % Cube10
Water Kg/m³180
Water % Cube18
Foam litres 50grms/l384
Foam % Cube38
Chemical litres @2.5%0.48
Strength N/mm2 @ 28 Days4.5
Thermal Insulation W/m.K0.47
Shrinkage %0.09
E modulus @ 90 days Mpa7800
Mix3;1;0.6
Wet Density Kg/m³1500
Sand 2mm max Kg/m³966
Sand % Cube37
Cement 52.5N Kg/m³322
Cement % Cube10
Water Kg/m³193
Water % Cube19
Foam litres 50grms/l338
Foam % Cube34
Chemical litres @2.5%0.43
Strength N/mm2 @ 28 Days5.7
Thermal Insulation W/m.K0.55
Shrinkage %0.08
E modulus @ 90 days Mpa9400
Mix3;1;0.6
Wet Density Kg/m³1600
Sand 2mm max Kg/m³1025
Sand % Cube39
Cement 52.5N Kg/m³340
Cement % Cube11
Water Kg/m³205
Water % Cube21
Foam litres 50grms/l292
Foam % Cube29
Chemical litres @2.5%0.36
Strength N/mm2 @ 28 Days7.3
Thermal Insulation W/m.K0.65
Shrinkage %0.07
E modulus @ 90 days Mpa11300
Mix3;1;0.6
Wet Density Kg/m³1700
Sand 2mm max Kg/m³1098
Sand % Cube42
Cement 52.5N Kg/m³366
Cement % Cube11
Water Kg/m³220
Water % Cube22
Foam litres 50grms/l247
Foam % Cube25
Chemical litres @2.5%0.31
Strength N/mm2 @ 28 Days9.3
Thermal Insulation W/m.K0.75
Shrinkage %0.05
E modulus @ 90 days Mpa13500
Mix3;1;0.6
Wet Density Kg/m³1800
Sand 2mm max Kg/m³1170
Sand % Cube44
Cement 52.5N Kg/m³390
Cement % Cube13
Water Kg/m³234
Water % Cube23
Foam litres 50grms/l200
Foam % Cube20
Chemical litres @2.5%0.25
Strength N/mm2 @ 28 Days12
Thermal Insulation W/m.K0.85
Shrinkage %0.04
E modulus @ 90 days Mpa16000

More information

Propump Consultancy Services

Propump Engineering foamed concrete specialists site visits and consultancy services
Propump Engineering foamed concrete specialists site visits and consultancy services

Propump news & articles

Foam concrete inline production system enable the most accurate and efficient method of manufacturing foam concretes on-site
Foam concrete inline production system enable the most accurate and efficient method of manufacturing foam concretes on-site

Why choose foamed concrete?

Foamed Concrete Applications include filling of sink holes and other ground movement to support the underside of structures
Foamed concrete Applications including the use of fluid and free flowing material for the use in ground stabilisation and mass infill

Projects by Propump

Foamed concrete used for Crossrail tunnelling works, foamed concrete filling addits, tunnels and TBM machines
Foamed concrete used for Crossrail tunnelling works, foamed concrete filling addits, tunnels and TBM machines