European Specifications

Neat Cement

Mix	0;1;0.6
Wet Density Kg/m³	300
Sand 2mm max Kg/m³	0
Sand % Cube	0
Cement 52.5N Kg/m³	160
Cement % Cube	5
Water Kg/m³	96
Water % Cube	10
Foam litres 50grms/l	852
Foam % Cube	85
Chemical litres @2.5%	1.06
Strength N/mm2 @ 28 Days	0.5
Thermal Insulation W/m.K	0.08
Shrinkage %	0.38
E modulus @ 90 days Mpa	300

Mix	0;1;0.6
Wet Density Kg/m³	400
Sand 2mm max Kg/m³	0
Sand % Cube	0
Cement 52.5N Kg/m³	225
Cement % Cube	7
Water Kg/m³	135
Water % Cube	14
Foam litres 50grms/l	794
Foam % Cube	79
Chemical litres @2.5%	1.0
Strength N/mm2 @ 28 Days	1.0
Thermal Insulation W/m.K	0.09
Shrinkage %	0.30
E modulus @ 90 days Mpa	600

Mix	0;1;0.6
Wet Density Kg/m³	500
Sand 2mm max Kg/m³	0
Sand % Cube	0
Cement 52.5N Kg/m³	290
Cement % Cube	9
Water Kg/m³	175
Water % Cube	18
Foam litres 50grms/l	734
Foam % Cube	73
Chemical litres @2.5%	0.92
Strength N/mm2 @ 28 Days	2.0
Thermal Insulation W/m.K	0.1
Shrinkage %	0.27
E modulus @ 90 days Mpa	1000

Mix	0;1;0.6
Wet Density Kg/m³	600
Sand 2mm max Kg/m³	0
Sand % Cube	0
Cement 52.5N Kg/m³	335
Cement % Cube	11
Water Kg/m³	210
Water % Cube	21
Foam litres 50grms/l	675
Foam % Cube	68
Chemical litres @2.5%	0.84
Strength N/mm2 @ 28 Days	3.0
Thermal Insulation W/m.K	0.11
Shrinkage %	0.22
E modulus @ 90 days Mpa	1600

Mix	0;1;0.6
Wet Density Kg/m³	700
Sand 2mm max Kg/m³	0
Sand % Cube	0
Cement 52.5N Kg/m³	420
Cement % Cube	13
Water Kg/m³	250
Water % Cube	25
Foam litres 50grms/l	616
Foam % Cube	62
Chemical litres @2.5%	0.77
Strength N/mm2 @ 28 Days	4.0
Thermal Insulation W/m.K	0.13
Shrinkage %	0.21
E modulus @ 90 days Mpa	2400

Mix	0;1;0.6
Wet Density Kg/m³	800
Sand 2mm max Kg/m³	0
Sand % Cube	0
Cement 52.5N Kg/m³	482
Cement % Cube	15
Water Kg/m³	290
Water % Cube	29
Foam litres 50grms/l	557
Foam % Cube	56
Chemical litres @2.5%	0.70
Strength N/mm2 @ 28 Days	5.0
Thermal Insulation W/m.K	0.15
Shrinkage %	0.20
E modulus @ 90 days Mpa	3300

1:1 Sand / Cement mix

Mix	1;1;0.6
Wet Density Kg/m³	600
Sand 2mm max Kg/m³	216
Sand % Cube	8
Cement 52.5N Kg/m³	216
Cement % Cube	7
Water Kg/m³	130
Water % Cube	13
Foam litres 50grms/l	719
Foam % Cube	72
Chemical litres @2.5%	0.90
Strength N/mm2 @ 28 Days	1.0
Thermal Insulation W/m.K	0.11
Shrinkage %	0.22
E modulus @ 90 days Mpa	1300

Mix	1;1;0.6
Wet Density Kg/m³	700
Sand 2mm max Kg/m³	256
Sand % Cube	10
Cement 52.5N Kg/m³	256
Cement % Cube	8
Water Kg/m³	153
Water % Cube	15
Foam litres 50grms/l	668
Foam % Cube	67
Chemical litres @2.5%	0.84
Strength N/mm2 @ 28 Days	1.5
Thermal Insulation W/m.K	0.13
Shrinkage %	0.21
E modulus @ 90 days Mpa	1800

Mix	1;1;0.6
Wet Density Kg/m³	800
Sand 2mm max Kg/m³	295
Sand % Cube	12
Cement 52.5N Kg/m³	295
Cement % Cube	9
Water Kg/m³	177
Water % Cube	17
Foam litres 50grms/l	617
Foam % Cube	62
Chemical litres @2.5%	0.77
Strength N/mm2 @ 28 Days	2
Thermal Insulation W/m.K	0.15
Shrinkage %	0.20
E modulus @ 90 days Mpa	2500

Mix	1;1;0.6
Wet Density Kg/m³	900
Sand 2mm max Kg/m³	335
Sand % Cube	13
Cement 52.5N Kg/m³	335
Cement % Cube	10
Water Kg/m³	200
Water % Cube	20
Foam litres 50grms/l	565
Foam % Cube	57
Chemical litres @2.5%	0.70
Strength N/mm2 @ 28 Days	3
Thermal Insulation W/m.K	0.17
Shrinkage %	0.19
E modulus @ 90 days Mpa	3500

Mix	1;1;0.6
Wet Density Kg/m³	1000
Sand 2mm max Kg/m³	375
Sand % Cube	14
Cement 52.5N Kg/m³	375
Cement % Cube	12
Water Kg/m³	224
Water % Cube	22
Foam litres 50grms/l	515
Foam % Cube	52
Chemical litres @2.5%	0.64
Strength N/mm2 @ 28 Days	4
Thermal Insulation W/m.K	0.2
Shrinkage %	0.18
E modulus @ 90 days Mpa	4500

2:1 Sand / Cement mix

Mix	2;1;0.6
Wet Density Kg/m³	700
Sand 2mm max Kg/m³	370
Sand % Cube	14
Cement 52.5N Kg/m³	185
Cement % Cube	6
Water Kg/m³	110
Water % Cube	11
Foam litres 50grms/l	690
Foam % Cube	69
Chemical litres @2.5%	0.86
Strength N/mm2 @ 28 Days	0.7
Thermal Insulation W/m.K	0.13
Shrinkage %	0.21
E modulus @ 90 days Mpa	1700

Mix	2;1;0.6
Wet Density Kg/m³	800
Sand 2mm max Kg/m³	426
Sand % Cube	16
Cement 52.5N Kg/m³	213
Cement % Cube	7
Water Kg/m³	127
Water % Cube	13
Foam litres 50grms/l	643
Foam % Cube	64
Chemical litres @2.5%	0.80
Strength N/mm2 @ 28 Days	0.90
Thermal Insulation W/m.K	0.15
Shrinkage %	0.20
E modulus @ 90 days Mpa	2300

Mix	2;1;0.6
Wet Density Kg/m³	900
Sand 2mm max Kg/m³	482
Sand % Cube	18
Cement 52.5N Kg/m³	241
Cement % Cube	8
Water Kg/m³	144
Water % Cube	14
Foam litres 50grms/l	596
Foam % Cube	60
Chemical litres @2.5%	0.75
Strength N/mm2 @ 28 Days	1.2
Thermal Insulation W/m.K	0.17
Shrinkage %	0.19
E modulus @ 90 days Mpa	2900

Mix	2;1;0.6
Wet Density Kg/m³	1000
Sand 2mm max Kg/m³	540
Sand % Cube	20
Cement 52.5N Kg/m³	270
Cement % Cube	9
Water Kg/m³	160
Water % Cube	16
Foam litres 50grms/l	548
Foam % Cube	55
Chemical litres @2.5%	0.68
Strength N/mm2 @ 28 Days	1.6
Thermal Insulation W/m.K	0.2
Shrinkage %	0.18
E modulus @ 90 days Mpa	3800

Mix	2;1;0.6
Wet Density Kg/m³	1100
Sand 2mm max Kg/m³	596
Sand % Cube	22
Cement 52.5N Kg/m³	298
Cement % Cube	10
Water Kg/m³	180
Water % Cube	18
Foam litres 50grms/l	500
Foam % Cube	50
Chemical litres @2.5%	0.62
Strength N/mm2 @ 28 Days	2.2
Thermal Insulation W/m.K	0.23
Shrinkage %	0.15
E modulus @ 90 days Mpa	4800

Mix	2;1;0.6
Wet Density Kg/m³	1200
Sand 2mm max Kg/m³	653
Sand % Cube	24
Cement 52.5N Kg/m³	326
Cement % Cube	11
Water Kg/m³	195
Water % Cube	20
Foam litres 50grms/l	453
Foam % Cube	45
Chemical litres @2.5%	0.57
Strength N/mm2 @ 28 Days	3
Thermal Insulation W/m.K	0.27
Shrinkage %	0.11
E modulus @ 90 days Mpa	6000

Mix	2;1;0.6
Wet Density Kg/m³	1300
Sand 2mm max Kg/m³	709
Sand % Cube	27
Cement 52.5N Kg/m³	354
Cement % Cube	11
Water Kg/m³	213
Water % Cube	21
Foam litres 50grms/l	405
Foam % Cube	41
Chemical litres @2.5%	0.50
Strength N/mm2 @ 28 Days	4
Thermal Insulation W/m.K	0.35
Shrinkage %	0.10
E modulus @ 90 days Mpa	7500

Mix	2;1;0.6
Wet Density Kg/m³	1400
Sand 2mm max Kg/m³	766
Sand % Cube	29
Cement 52.5N Kg/m³	383
Cement % Cube	12
Water Kg/m³	230
Water % Cube	23
Foam litres 50grms/l	358
Foam % Cube	36
Chemical litres @2.5%	0.45
Strength N/mm2 @ 28 Days	5.4
Thermal Insulation W/m.K	0.47
Shrinkage %	0.09
E modulus @ 90 days Mpa	9000

Mix	2;1;0.6
Wet Density Kg/m³	1500
Sand 2mm max Kg/m³	824
Sand % Cube	31
Cement 52.5N Kg/m³	412
Cement % Cube	13
Water Kg/m³	247
Water % Cube	25
Foam litres 50grms/l	309
Foam % Cube	31
Chemical litres @2.5%	0.38
Strength N/mm2 @ 28 Days	7.2
Thermal Insulation W/m.K	0.55
Shrinkage %	1.08
E modulus @ 90 days Mpa	10500

3:1 Sand / Cement mix

Mix	3;1;0.6
Wet Density Kg/m³	1100
Sand 2mm max Kg/m³	700
Sand % Cube	26
Cement 52.5N Kg/m³	235
Cement % Cube	8
Water Kg/m³	140
Water % Cube	14
Foam litres 50grms/l	520
Foam % Cube	52
Chemical litres @2.5%	0.65
Strength N/mm2 @ 28 Days	2.2
Thermal Insulation W/m.K	0.23
Shrinkage %	0.15
E modulus @ 90 days Mpa	4200

Mix	3;1;0.6
Wet Density Kg/m³	1200
Sand 2mm max Kg/m³	766
Sand % Cube	29
Cement 52.5N Kg/m³	255
Cement % Cube	8
Water Kg/m³	153
Water % Cube	15
Foam litres 50grms/l	475
Foam % Cube	48
Chemical litres @2.5%	0.60
Strength N/mm2 @ 28 Days	2.8
Thermal Insulation W/m.K	0.27
Shrinkage %	0.11
E modulus @ 90 days Mpa	5200

Mix	3;1;0.6
Wet Density Kg/m³	1300
Sand 2mm max Kg/m³	832
Sand % Cube	31
Cement 52.5N Kg/m³	277
Cement % Cube	9
Water Kg/m³	166
Water % Cube	17
Foam litres 50grms/l	430
Foam % Cube	43
Chemical litres @2.5%	0.54
Strength N/mm2 @ 28 Days	3.6
Thermal Insulation W/m.K	0.35
Shrinkage %	0.10
E modulus @ 90 days Mpa	6500

Mix	3;1;0.6
Wet Density Kg/m³	1400
Sand 2mm max Kg/m³	900
Sand % Cube	34
Cement 52.5N Kg/m³	300
Cement % Cube	10
Water Kg/m³	180
Water % Cube	18
Foam litres 50grms/l	384
Foam % Cube	38
Chemical litres @2.5%	0.48
Strength N/mm2 @ 28 Days	4.5
Thermal Insulation W/m.K	0.47
Shrinkage %	0.09
E modulus @ 90 days Mpa	7800

Mix	3;1;0.6
Wet Density Kg/m³	1500
Sand 2mm max Kg/m³	966
Sand % Cube	37
Cement 52.5N Kg/m³	322
Cement % Cube	10
Water Kg/m³	193
Water % Cube	19
Foam litres 50grms/l	338
Foam % Cube	34
Chemical litres @2.5%	0.43
Strength N/mm2 @ 28 Days	5.7
Thermal Insulation W/m.K	0.55
Shrinkage %	0.08
E modulus @ 90 days Mpa	9400

Mix	3;1;0.6
Wet Density Kg/m³	1600
Sand 2mm max Kg/m³	1025
Sand % Cube	39
Cement 52.5N Kg/m³	340
Cement % Cube	11
Water Kg/m³	205
Water % Cube	21
Foam litres 50grms/l	292
Foam % Cube	29
Chemical litres @2.5%	0.36
Strength N/mm2 @ 28 Days	7.3
Thermal Insulation W/m.K	0.65
Shrinkage %	0.07
E modulus @ 90 days Mpa	11300

Mix	3;1;0.6
Wet Density Kg/m³	1700
Sand 2mm max Kg/m³	1098
Sand % Cube	42
Cement 52.5N Kg/m³	366
Cement % Cube	11
Water Kg/m³	220
Water % Cube	22
Foam litres 50grms/l	247
Foam % Cube	25
Chemical litres @2.5%	0.31
Strength N/mm2 @ 28 Days	9.3
Thermal Insulation W/m.K	0.75
Shrinkage %	0.05
E modulus @ 90 days Mpa	13500

Mix	3;1;0.6
Wet Density Kg/m³	1800
Sand 2mm max Kg/m³	1170
Sand % Cube	44
Cement 52.5N Kg/m³	390
Cement % Cube	13
Water Kg/m³	234
Water % Cube	23
Foam litres 50grms/l	200
Foam % Cube	20
Chemical litres @2.5%	0.25
Strength N/mm2 @ 28 Days	12
Thermal Insulation W/m.K	0.85
Shrinkage %	0.04
E modulus @ 90 days Mpa	16000

More information

Propump Consultancy Services

Propump Engineering foamed concrete specialists site visits and consultancy services

Propump news & articles

Foam concrete inline production system enable the most accurate and efficient method of manufacturing foam concretes on-site

Why choose foamed concrete?

Foamed Concrete Applications include filling of sink holes and other ground movement to support the underside of structures — Foamed concrete Applications including the use of fluid and free flowing material for the use in ground stabilisation and mass infill

Projects by Propump

Foamed concrete used for Crossrail tunnelling works, foamed concrete filling addits, tunnels and TBM machines